PA6T/日本三井化学\t/C240 增强级

产品参数性能项目试验条件[状态]测试方法测试数据数据单位基本性能吸水率23℃,24小时在水里(2mmt,100℃)ASTM D-5700.2(2.8)%物理性能模具收缩率2mmtASTM D-9550.4(0.8)%比重ASTM D-7921.53机械性能洛氏硬度ASTM D-785110M scale弯曲模量dy(moist)ASTM D-79013000(9000)MPa弯曲强度dy(moist)ASTM D-790300(260)MPaIZOD缺口冲击强度dy(moist)ASTM D-25685(90)J/M拉伸伸长率dy(moist)ASTM D-6383(3)%拉伸强度dy(moist)ASTM D-638210(180)MPa电气性能损耗因数1016Hz,dyASTM D-1500.018介电常数1016Hz,dyASTM D-1504.5Dielectic beakdown voltagedyASTM D-14930KV/mm体积电阻率dyASTM D-2571016Ω.cm热性能玻璃转变温度85℃熔点310℃负荷挠曲温度ASTM D-648300℃阻燃性UL 94HB线性热膨胀系数ASTM D-6962.0(4.5)×10-5/℃其它性能Glass fibe content40%

产品细节图

产品参数性能项目试验条件[状态]测试方法测试数据数据单位基本性能吸水率23℃,24小时在水里(2mmt,100℃)ASTM D-5700.2(2.8)%物理性能模具收缩率2mmtASTM D-9550.4(0.8)%比重ASTM D-7921.53机械性能洛氏硬度ASTM D-785110M scale弯曲模量dy(moist)ASTM D-79013000(9000)MPa弯曲强度dy(moist)ASTM D-790300(260)MPaIZOD缺口冲击强度dy(moist)ASTM D-25685(90)J/M拉伸伸长率dy(moist)ASTM D-6383(3)%拉伸强度dy(moist)ASTM D-638210(180)MPa电气性能损耗因数1016Hz,dyASTM D-1500.018介电常数1016Hz,dyASTM D-1504.5Dielectic beakdown voltagedyASTM D-14930KV/mm体积电阻率dyASTM D-2571016Ω.cm热性能玻璃转变温度85℃熔点310℃负荷挠曲温度ASTM D-648300℃阻燃性UL 94HB线性热膨胀系数ASTM D-6962.0(4.5)×10-5/℃其它性能Glass fibe content40%

产品细节图